Structural, optical and nanomechanical properties of (111) oriented nanocrystalline ZnTe thin films

Structural, optical and nanomechanical properties of nanocrystalline Zinc Telluride (ZnTe) films of thickness upto 10 microns deposited at room temperature on borosilicate glass substrates are reported. X-ray diffraction patterns reveal that the films were preferentially oriented along the (1 1 1) direction. The maximum refractive index of the films was 2.74 at a wavelength of 2000 nm. The optical band gap showed strong thickness dependence. The average film hardness and Young's modulus obtained from load-displacement curves and analyzed by Oliver-Pharr method were 4 and 70 GPa respectively. Hardness of (1 1 1) oriented ZnTe thin films exhibited almost 5 times higher value than bulk. The studies show clearly that the hardness increases with decreasing indentation size, for indents between 30 and 300 nm in depth indicating the existence of indentation size effect. The coefficient of friction for these films as obtained from the nanoscratch test was ~0.4.

Structural, optical and nanomechanical properties of (111) oriented nanocrystalline ZnTe thin films, M.S.R.N. Kiran, S. Kshirsagar, M.G. Krishna and S.P. Tewari (2010), Eur. Phys. J. Appl. Phys. DOI 10.1051/epjap/2010071

Editors-in-Chief
David Blaschke, Thomas Duguet and Maria Jose Garcia Borge
It has been a pleasure to work with you since we submitted our draft last September, and I wanted to thank you for your help during all stages of the publication process. Please extend our gratitude to the whole EPJA team.

Manuel Zambrana, Institut fuer Kernphysik, University of Mainz, Germany

ISSN (Print Edition): 1434-6001
ISSN (Electronic Edition): 1434-601X

© Società Italiana di Fisica and
Springer-Verlag